PTFE sleeves manufactured as per MIL-1-22129 or JSS 54802 are for use in Electrical, Electronic, Chemical, Mechanical & other industries. PTFE Sleeves are inert to almost all chemicals, Oils, Fluxes etc. Wide temperature range from - 200°C to 260°C, long flex-life and high burst-strength. Smooth internal surface of PTFE sleeves allow closer fits. Can be offered with connector assemblies.

Advantages

High Performance from -200°C to 260°C (Peak 300°C)

Unaffected at soldering temperatures; Autoclavable

Suitable for High-Density wiring

Smooth Internals allow closer fit

Superior Tape-Wrapping-Sintering (TWS) Method provides good mechanical stability, high burst pressure and long flex-life

High Dielectric Strength

Resistant to UV Radiation

Fire non-propagating

Inert to almost all chemicals (few exceptions), solvents, fluxes, oils; Zero extractables

Freedom from Ageing, Fungus and Water Absorption

Biocompatible

Specifications

As per MIL-I-22129C USA Military Standards and JSS 54802 Indian Defence Standards; Type-Approved by Indian Defence Authorities since 1991

100% Inspected

Rated Break Down Voltages (BDV) as follows:

Wall Thickness	Break Down Voltage (AC RMS)
0.25mm	11.5 KV
0.30mm	14.6 KV
0.40mm	16.3 KV
0.50mm	17.0 KV

AWG SIZES (MIL-1-22129)

	inches					mm
AWG	Internal Diameter			Std. Wall Thickness		Internal Diameter			Std. Wall Thickness
	Nom.	MIN.	MAX.	Nom.	Tol.	Nom.	MIN.	MAX.	Nom.	Tol.
30	0.012	0.010	0.015	0.009	±0.002	0.30	0.25	0.38	0.23	±0.05
28	0.015	0.013	0.019	0.009	±0.002	0.38	0.33	0.48	0.23	±0.05
26	0.018	0.016	0.022	0.009	±0.002	0.46	0.41	0.56	0.23	±0.05
24	0.022	0.020	0.027	0.012	±0.002	0.56	0.51	0.69	0.30	±0.05
22	0.028	0.025	0.032	0.012	±0.002	0.71	0.64	0.81	0.30	±0.05
20	0.034	0.032	0.039	0.016	±0.003	0.86	0.81	0.99	0.41	±0.08
19	0.038	0.036	0.044	0.016	±0.003	0.97	0.91	1.12	0.41	±0.08
18	0.042	0.040	0.049	0.016	±0.003	1.07	1.02	1.24	0.41	±0.08
17	0.047	0.045	0.054	0.016	±0.003	1.19	1.14	1.37	0.41	±0.08
16	0.053	0.051	0.061	0.016	±0.003	1.35	1.30	1.55	0.41	±0.08
15	0.059	0.057	0.067	0.016	±0.003	1.50	1.45	1.70	0.41	±0.08
14	0.066	0.064	0.074	0.016	±0.003	1.68	1.63	1.88	0.41	±0.08
13	0.076	0.072	0.082	0.016	±0.003	1.93	1.83	2.08	0.41	±0.08
13	0.076	0.072	0.082	0.016	±0.003	1.93	1.83	2.08	0.41	±0.08
12	0.085	0.081	0.091	0.016	±0.003	2.16	2.06	2.31	0.41	±0.08
11	0.095	0.091	0.101	0.016	±0.003	2.41	2.31	2.57	0.41	±0.08
10	0.106	0.102	0.112	0.016	±0.003	2.69	2.59	2.84	0.41	±0.08
9	0.118	0.114	0.124	0.020	±0.004	3.00	2.90	3.15	0.51	±0.10
8	0.133	0.129	0.141	0.020	±0.004	3.38	3.28	3.58	0.51	±0.10
7	0.148	0.144	0.158	0.020	±0.004	3.76	3.66	4.01	0.51	±0.10
6	0.166	0.162	0.178	0.020	±0.004	4.22	4.11	4.52	0.51	±0.10
5	0.186	0.182	0.198	0.020	±0.004	4.72	4.62	5.03	0.51	±0.10
4	0.208	0.204	0.224	0.020	±0.004	5.28	5.18	5.69	0.51	±0.10
3	0.234	0.229	0.249	0.020	±0.004	5.94	5.82	6.32	0.51	±0.10
2	0.263	0.258	0.278	0.020	±0.004	6.68	6.55	7.06	0.51	±0.10
1	0.294	0.289	0.311	0.020	±0.004	7.47	7.34	7.90	0.51	±0.10
0	0.330	0.325	0.347	0.020	±0.004	8.38	8.26	8.81	0.51	±0.10